Sour service Pipe
Buy ISO 15156 Nace MR0175 Steel Pipes at factory price in Kolkata
Sour service can be defined as an exploration into environments producing oil, which contains enough H2S that, will ultimately cause cracking of metallic materials. Sour service pipe is used in environments having high corrosion resistance. Materials For Sour Service Pipeline include silicon, sulfur, carbon, phosphorous, manganese, titanium, vanadium, niobium, and elements in smaller quantities. This process should keep in mind the entire design process of the project, cost, maintenance, safety, risks, and environmental effects. We are proud to be the leading manufacturers of sour service pipe, and our ultimate aim is to produce high-quality products at reasonable rates.
Sour service Pipe
ISO 15156 Nace MR0175 Steel Pipes
Erw Pipe Sour Service
Erw Pipe Sour Service Supplier in India, Check Grade Sour Service Drill Pipes Weight Chart
Sour service drill pipe is used in well drilling applications. These pipes can either be welded or be seamless in formation. As the drilling process intensifies the possibility of hitting H2S increases. This may, in turn, lead to hydrogen-induced cracking in this sour environment. However, the presence of the sour service pipeline ensures that the hydrogen is kept under check and improves the mechanical properties of the line. These pipes are carbon steel pipes that are customized for sour services. The tensile strength of these pipes ranges from 415 MPa to 760 MPa and the yield strength is from 245 MPa- 635 MPa depending on the grade of the pipes.
The carbon steel pipe for sour service comes in 3/8 inches to 30 inches with different coatings. They are treated for heat and sub-zero temperatures. The seamless API 5L grade B pipe is mostly preferred; in sour gas services. Due to the acute shortage of the above pipe ERW, pipes are used as a replacement. The erw sour service has so far been able to control the service as long as quality control is maintained.
Table of Contents
- Specification List of Sour service Pipe
- Check Price of Sour Service Pipeline
- Material Chart of Erw Pipe Sour Service
- Sour Service Drill Pipes Inspection Frequency
- Various Types of Sour Service Line Pipe
- Chemical Structure of Sour services steel pipe
- Mechanical Behaviour of sour service drill pipe
- Hardness Tests of Sour service Pipe
Specification List of Sour service Pipe
| Finish | Black (Coated) |
| Nominal Pipe Size | 1/4" |
| Schedule | SCH 40 |
| Length | 21' |
| Metal | Steel |
| Type | Pipe |
| Features | High Strength, Corrosion Resistant, High Toughness and Deformability |
Check Price of Sour Service Pipeline
| Sour Service Pipe Price in India | Sour Service Pipe Price in INR | Sour Service Pipe Price in USD | Sour Service Pipe Price in UAE Dirham |
| PIPELINE HOT FINISHED SEAMLESS LINE PIPE SOUR SERVICE API SPEC 5L PSL 2 | Rs. 73 | 0.97 USD | UAE Dirham 3.58 |
Material Chart of Erw Pipe Sour Service
| No. | Grade | Specification | Executive Standard | ||
| Outer Diameter /mm | Wall Thickness /mm | Economical Length/m | |||
| 1 | BNS PSL2 X42NS PSL2 X46NS PSL2 X52NS PSL2 |
10 ~ 127 | 1 ~ 20 | 6 ~ 12.0 | API 5L Line Pipe Standard |
| 42 ~ 114.3 | 3.5 ~ 8 | 6 ~ 12.2 | |||
| 60 ~ 114.3 | 8 ~ 12 | 6 ~ 12.2 | |||
| 114.3 ~ 180 | 3.8 ~ 14 | 6 ~ 12.2 | |||
| 114.3 ~ 180 | 14 ~ 22 | 6 ~ 12.2 | |||
| 68 ~ 232 | 10 ~ 20 | 6 ~ 12.2 | |||
| 76 ~ 254 | 20 ~ 55 | 6 ~ 12.2 | |||
| 140 ~ 368 | 6 ~ 14 | 6 ~ 12.2 | |||
| 140 ~ 368 | 14 ~ 42 | 6 ~ 12.2 | |||
| 318 ~ 720 | 14 ~ 120 | 4 ~ 12.5 | |||
| 2 | BQS PSL2 X42QS PSL2 |
42 ~ 114.3 | 3.5 ~ 12 | 6 ~ 12.2 | |
| 114.3 ~ 180 | 3.8 ~ 22 | 6 ~ 12.2 | |||
| 68 ~ 254 | 10 ~ 30 | 6 ~ 12.2 | |||
| 140 ~ 368 | 6 ~ 30 | 6 ~ 12.2 | |||
| 318 ~ 720 | 14 ~ 30 | 4 ~ 12.5 | |||
| 3 | X46QS PSL2 X52QS PSL2 X56QS PSL2 X60QS PSL2 |
42 ~ 114.3 | 3.5 ~ 12 | 6 ~ 12.2 | |
| 114.3 ~ 180 | 3.8 ~ 22 | 6 ~ 12.2 | |||
| 68 ~ 254 | 10 ~ 30 | 6 ~ 12.2 | |||
| 140 ~ 368 | 6 ~ 30 | 6 ~ 12.2 | |||
| 318 ~ 720 | 14 ~ 30 | 4 ~ 12.5 | |||
| 4 | X65QS PSL2 X70QS PSL2 |
42 ~ 114.3 | 3.5 ~ 12 | 6 ~ 12.2 | |
| 114.3 ~ 180 | 3.8 ~ 22 | 6 ~ 12.2 | |||
| 68 ~ 254 | 10 ~ 25 | 6 ~ 12.2 | |||
| 140 ~ 368 | 6 ~ 25 | 6 ~ 12.2 | |||
| 318 ~ 720 | 14 ~ 25 | 4 ~ 12.5 | |||
Buy Carbon Steel Pipe For Sour Service at factory price
Sour Service Drill Pipes Inspection Frequency
| Type of inspection | Type of pipe | Frequency of inspection |
| Hardness testing of Pipes with D < 508 mm (20.000 in) |
SMLS,HFW, SAWL, or SAWH | Once per test unit of not more than 100 lengths of Pipes with the same cold-expansion ratio a |
| Hardness testing of Pipes with D ≥ 508 mm (20.000 in) |
SMLS,HFW, SAWL, or SAWH | Once per test unit of not more than 50 lengths of Pipes with the same cold-expansion ratio a |
| Hardness testing of hard spots in welded Pipes | HFW, SAWL, or SAWH | Each hard spot found on the internal or external surface of the Pipes |
| if agreed, hardness testing of the longitudinal or helical-seam weld of welded Pipes | HFW, SAWL, or SAWH | As specified in the purchase order |
| pipe diameter and out-of-roundness for Pipes with D ≤ 168,3 mm (6.625 in) |
SMLS,HFW, SAWL, or SAWH | Once per test unit of not more than 100 lengths of Pipes |
| pipe diameter and out-of-roundness for Pipes with D> 168,3 mm (6.625 in) |
SMLS,HFW, SAWL, or SAWH | Once per test unit of not more than 20 lengths of Pipes |
| Non-destructive inspection | SMLS,HFW, SAWL, or SAWH | In accordance with Annex K |
| HIC test | SMLS,HFW, SAWL, or SAWH | One test for each of the first three heats applied; thereafter, one test for each test unit of not more than ten heats of steel |
| if agreed, SSC test | SMLS,HFW, SAWL, or SAWH | One test for each pipe provided for manufacturing procedure qualification |
Various Types of Sour Service Line Pipe
sour services pipe API 5L
sour service drill pipe
sour service line pipe
Sour services steel pipe
carbon steel pipe for sour service
Sour Service BQS STEEL PIPE
Sour service pipe used in low temperature
14.27mm THK API 5L sour service Pipe
Chemical Structure of Sour services steel pipe
| Steel grade | Mass fraction, based upon heat and product analyses % maximum |
Carbon equivalent a % maximum |
|||||||||
| C b | Si | Mn b | P | S | V | Nb | Ti | Other c, d | CE llw | CE pcm | |
| SMLS and welded pipes | |||||||||||
| L245NS or BNS | 0,14 | 0,40 | 1,35 | 0,020 | 0,003 e | f | f | 0,04 | g | 0,36 | 0,19 h |
| L290NS or X42NS | o,14 | 0,40 | 1,35 | 0,020 | 0,003 e | 0,05 | 0,05 | 0,04 | - | 0,36 | 0,19 h |
| L320NS or X46NS | 0,14 | 0,40 | 1,40 | 0,020 | 0,003 e | 0,07 | 0,05 | 0,04 | g | 0,38 | 0,20 h |
| L360NS or X52NS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,10 | 0,05 | 0,04 | g | 0,43 | 0,22 h |
| L245QS or BQS | 0,14 | 0,40 | 1,35 | 0,020 | 0,003 e | 0,04 | 0,04 | 0,04 | - | 0,34 | 0,19 h |
| L 290QS or X42QS | 0,14 | 0,40 | 1,35 | 0,020 | 0,003 e | 0,04 | 0,04 | 0,04 | - | 0,34 | 0,19 h |
| L320QS or X46QS | 0,15 | 0,45 | 1,40 | 0,020 | 0,003 e | 0,05 | 0,05 | 0,04 | - | 0,36 | 0,20 h |
| L360QS or X52QS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,07 | 0,05 | 0,04 | g | 0,39 | 0,20 h |
| L390QS or X56QS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,07 | 0,05 | 0,04 | g | 0,40 | 0,21 h |
| L415QS or X60QS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,08 | 0,05 | 0,04 | g,i,k | 0,41 | 0,22 h |
| L450QS or X65QS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,09 | 0,05 | 0,06 | g,i,k | 0,42 | 0,22 h |
| L485QS or X70QS | 0,16 | 0,45 | 1,65 | 0,020 | 0,003 e | 0,09 | 0,05 | 0,06 | g,i,k | 0,42 | 0,22 h |
| welded pipe | |||||||||||
| L245MS or BMS | 0,10 | 0,40 | 1,25 | 0,020 | 0,002 e | 0,04 | 0,04 | 0,04 | - | - | 0,19 |
| L290MS or X42MS | 0,10 | 0,40 | 1,25 | 0,020 | 0,002 e | 0,04 | 0,04 | 0,04 | - | - | 0,19 |
| L320MS or X46 MS | 0,10 | 0,45 | 1,35 | 0,020 | 0,002 e | 0,05 | 0,05 | 0,04 | - | - | 0,20 |
| L360MS or X52 MS | 0,10 | 0,45 | 1,45 | 0,020 | 0,002 e | 0,05 | 0,06 | 0,04 | - | - | 0,20 |
| L390MS or X56 MS | 0,10 | 0,45 | 1,45 | 0,020 | 0,002 e | 0,06 | 0,08 | 0,04 | g | - | 0,21 |
| L415MS or X60 MS | 0,10 | 0,45 | 1,45 | 0,020 | 0,002 e | 0,08 | 0,08 | 0,06 | g,i | - | 0,21 |
| L450MS or X65MS | 0,10 | 0,45 | 1,60 | 0,020 | 0,002 e | 0,10 | 0,08 | 0,06 | g,i,j | - | 0,22 |
| L485MS or X70 MS | 0,10 | 0,45 | 1,60 | 0,020 | 0,002 e | 0,10 | 0,08 | 0,06 | g,i,j | - | 0,22 |
Stockist of Sour Service Line Pipe
Mechanical Behaviour of sour service drill pipe
| Pipe steel grade | Pipe body of SMLS and welded pipes | Weld seam of HFW and SAW pipes | |||||
| Yield strength a Rto,5 Mpa (psi) |
Tensile strength a Rm Mpa (psi) |
Ratio b Rto,5/Rm |
Elongation on 50 mm or 2 in Af % |
Tensile strength c |
|||
| minimum | maximum | minimum | maximum | maximum | minimum | minimum | |
| L245NS or BNS L245QS or BQS L245MS or BMS |
245 (35 500) |
450 d (65 300) d |
415 (60 200) |
760 (110 200) |
0,93 | e | 415 (60 200) |
| L290NS or X42NS L290QS or X42QS L290MS or X42MS |
290 (42 100) |
495 (71 800) |
415 (60 200) |
760 (110 200) |
0,93 | e | 415 (60 200) |
| L320NS or X46NS L320QS or X46QS L320MS or X46MS |
320 (46 400) |
525 (76 100) |
435 (63 100) |
760 (110 200) |
0,93 | e | 435 (63 100) |
| L360NS or X52NS L360QS or X52QS L360MS or X52MS |
|
530 (76 900) |
460 (66 700) |
760 (110 200) |
0,93 | e | 460 (66 700) |
| L390QS or X56QS L390MS or X56MS |
390 (56 600) |
545 (79 000) |
490 (71 100) |
760 (110 200) |
0,93 | e | 490 (71 100) |
| L415QS or X60QS L415MS or X60MS |
415 (60 200) |
565 (81 900) |
520 (75 400) |
760 (110 200) |
0,93 | e | 520 (75 400) |
| L450QS or X65QS L450MS or X65MS |
450 (65 300) |
600 (87 000) |
535 (77 600) |
760 (110 200) |
0,93 | e | 535 (77 600) |
| L485MS or X70MS | 485 (70 300) |
635 (92 100) |
570 (82 700) |
760 (110 200) |
0,93 | e | 570 (82 700 |
Quality-oriented Sour services steel pipe Exporter in India
Hardness Tests of Sour service Pipe
| Type of pipe | Sample location | Number, orientation and location of test pieces per sample a | |
| Specified outside diameter D mm (in) |
|||
| < 508 (20.000) | ≥ 508 (20.000) | ||
| SMLS b (see Figure 5 a ) | pipe body | 1T | 1T |
| SAWL (see Figure 5 b ) | seam weld | 1W | 1W c |
| SAWH (see Figure 5 c ) | seam weld | 1W | 1W |
| SAWH (see Figure 5 c ) | strip/plate end weld | 1WS | 1WS |
| HFW (see Figure 5 b ) | seam weld | 1W | 1W |